High strength TStE380 carbon steel plate sheet with 5000-18000mm length

What are the characteristics of medium and thick plate, TStE380 carbon steel plate sheet? First, the performance of shock resistance and vibration is very good, so the application of medium and thick plates in buildings and bridges can greatly improve the safety. Second, the bearing capacity of medium and thick plate, TStE380 carbon steel plate sheet is good, the performance is excellent. The bridge, the automobile girder steel plate, and buildings have strict load-bearing requirements, and it is easy to cause accidents if the steel materials not meet the requirements, so the selection of steel is more stringent.

The toughness of steel such as TStE380 carbon steel plate sheet is the ability of steel to absorb energy in the process of plastic deformation and fracture, and also the ability of steel to resist impact load. It is related to and different from the plasticity of steel. It is the comprehensive performance of strength and plasticity. The strength plasticity index of steel is obtained by static tensile test. When these indexes are used to bear the dynamic load structure, there are obvious limitations.

A514 grade Q alloy structural steel chemical composition (melting analysis)%C: 0.14-0.21, Si: 0.15-0.35, Mn: 0.95-1.30, P max.: 0.035, S max.: 0.035, Ni: 1.20-1.50, Cr: 1.00-1.50, Mo: 0.45-0.6.0, V: 0.03-0.08The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18

The main applications of normalizing are as follows:① For low carbon steel, TStE380 carbon steel plate sheet. The hardness of low carbon steel after normalizing is slightly higher than that after annealing, and the toughness is also better, so normalizing can be used as the pretreatment of cutting.② For medium carbon steel, normalizing can be used as the final heat treatment instead of quenching and tempering treatment, or as the preparation treatment before surface quenching by induction heating.③ Normalizing can be used in tool steel, bearing steel, carburizing steel and so on, which can eliminate or inhibit the formation of network carbide, thus obtaining the good microstructure needed for spheroidizing annealing.④ Normalizing can refine the cast structure and improve the machinability of steel castings.