Main application of JIS carbon steel SM490A CS plate

10 to 20mm thick JIS carbon steel SM490A CS plate product: 10*2200*7200, 10*2200*8000, 12*2000*11850, 12.5*2900*11000, 12.9*2987*10384, 13.6*2940*11455, 14*2000*10000, 14*2000*11181, 14*2000*13500, 14*2070*9060, 14*2200*10030, 15*2200*10270, 15*2500*10000, 15*2992*10185, 16*1500*9340, 16*1800*6000, 16*2000*10713, 16*2120*6080, 16*2200*10000, 16*2230*7650, 18.5*2320*6600, 20*1400*11400, 20*2100*7000.

Non-destructive flaw detection of steel plates is a test method for inspecting the JIS carbon steel SM490A CS plate surface and internal quality of the inspected parts without damaging the working state of the workpiece or raw materials. Commonly used JIS carbon steel SM490A CS plate steel plate flaw detection methods include: X-ray flaw detection, ultrasonic flaw detection, magnetic particle flaw detection, penetration flaw detection, eddy current flaw detection, gamma-ray flaw detection, fluorescent flaw detection, color flaw detection and other methods. Physical flaw detection is non-destructive flaw detection without any chemical changes.

S50C steel characteristics: the carbon content of the steel (mass fraction, %) ≥ 0.4, excellent wear resistance, reduced ductility, easy to deform and crack after quenching, so quenching is extremely important, and it must be quenched after cutting and tempering to avoid tempering brittleness. By implementing spheroidizing treatment, the cutting performance of this type of carbon steel JIS carbon steel SM490A CS plate can be improved. The steel is usually used after tempering to a hardness of 19~22HRC to increase its cutting performance.

How to prevent JIS carbon steel SM490A CS plate, steel plate cutting cracks? 1. Preheat the steel plate before cutting, and the preheating temperature depends on the quality grade and thickness of the steel plate. However, it needs to be heated evenly. 2. The cutting speed is reduced appropriately, but its reliability is not as good as preheating. It is suggested to preheat the cutting belt with flame gun cavitation several times before cutting, and the preheating temperature should reach about 180℃.