2300 ton SA709 grade 50 carbon steel plate sheet supplied to Philippines

The SA709 grade 50 carbon steel plate sheet processing performance is good. Due to the uniform control of steel plate performance, excellent performance coordination and good toughness guarantee, the steel plate bending processing, drilling, cutting and other mechanical processing properties are excellent. In addition, the surface of the SA709 grade 50 carbon steel plate sheet steel plate is smooth and beautiful by inhibiting and removing oxide scale from slab heating to rolling process and heat treatment in furnace without oxidation atmosphere.

SA709 grade 50 carbon steel plate sheet 5mm to 10mm stock size5.5*2900*7400, 8*2400*6000, 9*2500*9500, 5*3000*5200, 6*2350*6300, 10*2000*6500, 8*2400*8000, 7*3000*6600, 6*2350*7400, 10*2150*5500, 8*2300*9000, 8*2400*8000, 6*2350*7200, 10*2550*10500, 8*2490*7200, 8*1800*10000, 10*2360*7700, 10*2490*8400, 9*2500*7400, 8*1800*8000, 10*2450*8000, 10*2100*11000, 10*2450*8000, 10*1650*9020.

A514 grade P alloy structural steel chemical composition (melting analysis)%C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.45-0.70, P max.: 0.035, S max.: 0.035, Ni: 1.20-1.50, Cr: 0.85-1.20, Mo: 0.45-0.6.0, B: 0.001-0.005The mechanical properties in thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18

The main applications of normalizing are as follows:① For low carbon steel, SA709 grade 50 carbon steel plate sheet. The hardness of low carbon steel after normalizing is slightly higher than that after annealing, and the toughness is also better, so normalizing can be used as the pretreatment of cutting.② For medium carbon steel, normalizing can be used as the final heat treatment instead of quenching and tempering treatment, or as the preparation treatment before surface quenching by induction heating.③ Normalizing can be used in tool steel, bearing steel, carburizing steel and so on, which can eliminate or inhibit the formation of network carbide, thus obtaining the good microstructure needed for spheroidizing annealing.④ Normalizing can refine the cast structure and improve the machinability of steel castings.