Do you know the A573 Gr 70 carbon steel materialyield strength?

Since its establishment, the company has always adhered to the enterprise spirit of "solid feet and lofty ideals, dare to create and take responsibility, and dedicate to work". After years of careful management, the company has achieved the double improvement of A573 Gr 70 carbon steel material capital strength and scale expansion, gained wide recognition and general praise from all walks of life, further realized specialized and large-scale operation and optimized allocation of resources, and effectively improved the A573 Gr 70 carbon steel material overall strength, competitiveness and anti risk ability of the company.

Our company produces ordinary carbon steel A573 Gr 70 carbon steel material with high strength and good plasticity and toughness. Due to the effect of alloy elements, its strength is 25% - 50% higher than that of ordinary carbon steel, its elongation is 15% - 23%, and its impact toughness at room temperature is higher than 60j / cm 2. We have a A573 Gr 70 carbon steel material production line specializing in the production of ordinary carbon steel plate, and strictly control its quality.

Chemical composition of A573 Gr 70 carbon steel material, Q345D steel plate: C: ≤0.18; Si: ≤0.50; Mn: ≤1.70; P: ≤0.030; S: ≤0.025; Nb: ≤0.07; V: ≤0.15; Ti: ≤0.20; Cr: ≤0.30; Ni: ≤0.50; Cu: ≤0.30; N: ≤0.012; Mo: ≤0.10; Als: ≥0.015. Yield strength (MPa) of Q345D steel plate: ≤16mm: ≥345; 16-40mm: ≥335; 40-63mm: ≥325; 63-80mm: ≥315; 80-100mm: ≥305; 100-150mm: ≥285; 150-200mm: ≥275; 200-250: ≥275; 250-400: ≥265. Tensile strength of Q345D low alloy steel: 450-630(MPa). Elongation: ≥21. Impact test: -20 ℃: ≥34.

We should focus on the main problems to be solved and pay attention to efficiency. After receiving the user's quality objection report data, the possible causes, responsible units, compensation amount, etc. of the problem shall be judged based on experience. To have a clear service plan, to be clear about what your main problem is, what technical support is needed, these should be prepared.